2014 aluminium is a 2000-series aluminium alloy: the main alloying addition is copper, and it is formulated for primary forming into wrought prodsucts. Aluminium alloys have strong corrosion resistance characteristics and high electrical conductivity. The strength of these alloys increases at subzero temperatures and strength is lost when these alloys are exposed to high temperatures. 2014 Aluminium alloy is widely used in aircraft structure, rivets, truck wheel, screw elements，and other various structures.
Prodsuct specification
OD：3MM to 500MM
Width: 12mm to 500mm, Custom Width Can be Cut from Plates
Length: Custom Lengths Available
Cut to Size Flat Bars, Round Bars, Blocks Available On Request
Finish：Mill Finish, Polished, Close Tolerance Polished Rods and Bars, Anodized
Application:2014 aluminum rodss are mainly used in aircraft structures, rivets, truck wheels, propeller components, and other various structural parts
Chemical Composition
| Alloy | Si | Fe | Cu | Mn | Mg |
| 2014 | 0.5-1.2 | 0.7 | 3.9-5.0 | 0.1-1.2 | 0.2-0.8 |
| Cr | Zn | Ti | Other each | Other total | Al. |
| 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | Remainder |
Mechanical Properties
| Grade | Temper | Diameter/mm | Tensile Strength Rm/MPa | Yield Strength Rp0.2/MPa | Elongation/% |
| 2014/2014A | T4、T4510、T4511 | ≤25 | ≥370 | ≥230 | ≥13 |
| ＞25~75 | ≥410 | ≥270 | ≥12 | ||
| ＞75~150 | ≥390 | ≥250 | ≥10 | ||
| ＞150~200 | ≥350 | ≥230 | ≥8 | ||
| T6,T6510,T6511 | ≤25 | ≥415 | ≥370 | ≥6 | |
| ＞25~75 | ≥460 | ≥415 | ≥7 | ||
| ＞75~150 | ≥465 | ≥420 | ≥7 | ||
| ＞150~200 | ≥430 | ≥350 | ≥6 | ||
| ＞200~250 | ≥420 | ≥320 | ≥5 |