Prodsuct Introdsuction
The 5083 aluminum alloy is a high-magnesium alloy with good strength in the non-heat treatable alloy, and good corrosion resistance and machinability. The surface is beautiful after anodizing. The arc welding performance is good. The main alloying element in the 5083 alloy is magnesium, which has good corrosion resistance and weldability, as well as moderate strength. Excellent corrosion resistance makes the 5083 alloy widely used in marine applications such as ships, as well as in automobiles, aircraft welding parts, subway light rails, pressure vessels that require strict fire protection (such as liquid tankers, refrigerated trucks, refrigerated containers), refrigeration units, TV towers, Drilling equipment, transportation equipment, missile parts, armor, etc.
Chemical Composition
Aluminum Al: balance
Silicon Si: 0.4
Copper Cu : 0.1
Magnesium Mg: 4.0--4.9
Zinc Zn: 0.25
Manganese Mn: 0.40--0.10
Titanium Ti : 0.15
Chromium Cr: 0.05--0.25
Iron Fe: 0.4
Single: 0.05
Total: 0.15
Mechanical Property
Tensile strength σb (MPa): 110-136
Elongation δ10 (%): ≥20
The annealing temperature was 415 °C.
Yield strength σs (MPa) ≥110
Sample blank size All wall thickness
Elongation δ5 (%) ≥12