7005-T6 aluminum is 7005 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. The graph barss on the material properties cards below compare 7005-T6 aluminum to: 7000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bars means this is the highest value in the relevant set. A half-full bars means it’s 50% of the highest, and so on.
Aluminum alloys are highly resistant to corrosion. They are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F), and tend to lose some of their strength. However, the strength of Aluminium / Aluminum alloys can be enhanced at subzero temperatures, thus making them good low-temperature alloys. Aluminium / Aluminum 7005 alloy is a wrought alloy type. The following datasheet will provide more details about Aluminium / Aluminum 7005 alloy.
7005 aluminum sheet sheet belongs to the Al-Zn-Mg-Cu super hard aluminum, good welding performance, heat treatment can be strengthened, the strength is less than 6061, but it is lighter as a typical lightweight aluminum. 7005 Aluminum Alloy sheet sheet often used in making welded structure have both high strength and high fracture toughness, such as transport vehicles, truss rods, container; large heat exchanger, and after welding can not be solid melt processing components; also can be used in the manufacture of sports equipment such as tennis racket and baseball bat.