7075 T6 Aluminum Forging Disc

Last Updated: 2023-09-26

1.Prodsuct Description


7075 T6 Aluminum Forging Disc

7075 aluminium alloy is an aluminium alloy, with zinc as the primary alloying element. It has excellent mechanical properties, and exhibits good ductility, high strength, toughness and good resistance to fatigue. It is more susceptible to embrittlement than many other aluminium alloys because of microsegregation, but has significantly better corrosion resistance than the 2000 alloys. It is one of the most commonly used aluminium alloy for highly stressed structural applications, and has been extensively utilized in aircraft structural parts.


2.Prodsuct Description



Chemical composition
AlloySiFeCuMnMgGrZnTiAl
70750.40.51.2-2.00.32.1-2.90.18-0.285.1-6.10.2balance



3.Prodsuct Application


7075 aluminium alloy's composition roughly includes 5.6–6.1% zinc, 2.1–2.5% magnesium, 1.2–1.6% copper, and less than a half percent of silicon, iron, manganese, titanium, chromium, and other metals. It is prodsuced in many tempers, some of which are 7075-0, 7075-T6, 7075-T651.   Aircraft fittings, gears and shafts, fuse parts, meter shafts and gears, missile parts, regulating valve parts, worm gears, keys, aircraft, aerospace and defense applications; bike frames, all terrain vehicle (ATV) sprockets.


4.Prodsuct Feature


T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%.

The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then aging at 120 °C for 24 hours. This yields the peak strength of the 7075 alloy. The strength is derived mainly from finely dispersed eta and eta' precipitates both within grains and along grain boundaries